| 15-5 PH | AM-350 |
| 17-4 PH | AM-355 |
| 17-7 PH | Custom 450 |
| PH 14-8 MO | Custom 455 |
| PH 15-7 MO | Maraging 250 |
| A-286 | Maraging 300 |
| AMS 2759/3 TABLE III | ||||
ALLOY |
CONDITION |
HARDNESS |
FORM (1) |
TENSILE PSI |
HRC |
(MPa) |
|||
H 900 |
40 TO 47 |
B,F,T,BI |
190,000 (1310) |
|
AND |
H 900 |
40 TO 47 |
SSP |
190,000 (1310) |
17-4 PH [UP] |
H 900 |
40 TO 47 |
C |
180,000 (1240) |
H 925 |
38 TO 45 |
B,F,T,BI |
180,000 (1240) |
|
H 925 |
38 TO 45 |
SSP |
170,000 (1175) |
|
H 925 |
38 TO 45 |
C |
170,000 (1175) |
|
H 950 |
37 TO 44 |
WROUGHT |
165,000 (1140) |
|
H 1000 |
36 TO 43 |
C |
150,000 (1035) |
|
H 1025 |
34 TO 42 |
B,F,T,BI |
155,000 (1070) |
|
H 1025 |
34 TO 42 |
SSP |
155,000 (1070) |
|
H 1050 |
32 TO 38 |
B,F,T,BI |
150,000 (1035) |
|
H 1075 |
31 TO 38 |
B,F,T,BI |
145,000 (1000) |
|
H 1075 |
31 TO 38 |
SSP |
145,000 (1000) |
|
H 1100 |
30 TO 37 |
B,F,T,BI |
140,000 (965) |
|
H 1100 |
30 TO 37 |
SSP |
140,000 (965) |
|
H 1100 |
30 TO 37 |
C |
130,000 (895) |
|
H 1150 |
28 TO 37 |
B,F,T,BI |
135,000 (930) |
|
H 1150 |
28 TO 37 |
SSP |
135,000 (930) |
|
H 1150M |
24 TO 30 |
ALL |
||
| 17-7 PH [UP] | RH 950 |
42 TO 49 |
SS |
210,000 (1450) |
RH 950 |
42 TO 49 |
P |
200,000 (1380) |
|
RH 950 |
42 TO 49 |
B |
185,000 (1275) |
|
RH 1000 |
41 TO 46 |
|||
RH 1050 |
40 TO 45 |
SSP |
180,000 (1240) |
|
RH 1050 |
40 TO 45 |
B |
170,000 (1175) |
|
RH 1075 |
38 TO 43 |
|||
RH 1100 |
34 TO 40 |
WROUGHT |
150,000 (1035) |
|
TH 950 |
42 TO 48 |
|||
TH 1000 |
40 TO 46 |
|||
TH 1050 |
38 TO 44 |
SSP,WT |
180,000 (1240) |
|
TH 1050 |
38 TO 44 |
B |
170,000 (1178) |
|
TH 1075 |
37 TO 42 |
|||
TH 1100 |
34 TO 39 |
|||
CH 900 |
46 MIN |
SS |
(2) |
|
| PH 14-8 MO [UP] | SRH 950 |
45 TO 51 |
SSP |
220,000 (1520) |
SRH 1050 |
38 TO 45 |
SSP |
200,000 (1380) |
|
| PH 15-7 MO [UP] | RH 950 |
46 TO 50 |
SSP |
225,000 (1555) |
RH 950 |
46 TO 50 |
B |
200,000 (1300) |
|
RH 1000 |
42 TO 46 |
|||
RH 1100 |
34 TO 42 |
|||
TH 1000 |
SSP |
205,000 (1415) |
||
TH 1050 |
40 TO 46 |
SSP |
190,000 (1310) |
|
TH 1050 |
40 TO 46 |
B |
170,000 (1175) |
|
TH 1075 |
39 TO 44 |
|||
TH 1100 |
36 TO 41 |
|||
CH 900 |
46 MIN |
SS |
240,000 (1655) |
|
| A-286 [UP] | 24 TO 35 |
SHEET, P |
125,000 (860 MPA) |
|
24 TO 36 |
ALL |
130,000 (895 MPA) |
||
24 TO 37 |
SHEET, P |
135,000 (930 MPA) |
||
24 TO 38 |
SHEET, P |
140,000 (965 MPA) |
||
29 TO 38 |
B,F |
140,000 (965 MPA) |
||
40 MIN |
B, WIRE |
200,000 (1380 MPA) |
||
| AM-350 [UP] | SCT 850 |
41 TO 48 |
SSP,T |
185,000 (1278) |
SCT 950 |
38 TO 45 |
SSP,T |
170,000 (1175) |
|
SCT1000 |
36 TO 43 |
B,F,T |
165,000 (1140) |
|
SCT 1100 |
35 TO 42 |
|||
| AM-355 [UP] | SCT 850 |
41 TO 47 |
SSP |
190,000 (1310) |
SCT 1000 |
37 TO 43 |
B,F,T |
170,000 (1175) |
|
SCT 1000 |
38 TO 44 |
SSP |
165,000 (1140) |
|
| CUSTOM 450 [UP] | H 900 |
39 MIN |
WROUGHT |
180,000 (1240) |
H 950 |
37 MIN |
|||
H 1000 |
36 MIN |
|||
H 1050 |
34 MIN |
WROUGHT |
145,000 (1000) |
|
H 1100 |
30 MIN |
|||
H 1150 |
26 MIN |
|||
| CUSTOM 455 [UP] | H 900 |
47 MIN |
||
H 950 |
45 MIN |
WROUGHT |
225,000 (1555) |
|
H 1000 |
44 MIN |
WROUGHT |
200,000 (1380) |
|
| MARAGING 250 [UP] | AGED |
49 TO 52 |
||
| MARAGING 300 [UP] | AGED |
52 TO 56 |
||
NOTE (1) |
B - BAR | F - FORGINGS |
T - TUBING | Bi - BILLET |
SSP - SHEET, STRIP, PLATE |
P - PLATE |
WT - WELDED TUBING | ||
NOTE (2) |
VARIES WITH THICKNESS | |||