AMS 2759/3 TABLE III

PAGE 1 OF 2

ALLOY

CONDITION

HARDNESS

FORM (1)

TENSILE PSI

ALLOY

CONDITION

HARDNESS

FORM (1)

TENSILE PSI

HRC

(MPa)

HRC

(MPa)

15-5 PH

H 900

40 TO 47

B,F,T,BI

190,000 (1310)

17-7 PH

RH 950

42 TO 49

SS

210,000 (1450)

AND

H 900

40 TO 47

SSP

190,000 (1310)

RH 950

42 TO 49

P

200,000 (1380)

17-4 PH

H 900

40 TO 47

C

180,000 (1240)

RH 950

42 TO 49

B

185,000 (1275)

H 925

38 TO 45

B,F,T,BI

180,000 (1240)

RH 1000

41 TO 46

H 925

38 TO 45

SSP

170,000 (1175)

RH 1050

40 TO 45

SSP

180,000 (1240)

H 925

38 TO 45

C

170,000 (1175)

RH 1050

40 TO 45

B

170,000 (1175)

H 950

37 TO 44

WROUGHT

165,000 (1140)

RH 1075

38 TO 43

H 1000

36 TO 43

C

150,000 (1035)

RH 1100

34 TO 40

WROUGHT

150,000 (1035)

H 1025

34 TO 42

B,F,T,BI

155,000 (1070)

TH 950

42 TO 48

H 1025

34 TO 42

SSP

155,000 (1070)

TH 1000

40 TO 46

H 1050

32 TO 38

B,F,T,BI

150,000 (1035)

TH 1050

38 TO 44

SSP,WT

180,000 (1240)

H 1075

31 TO 38

B,F,T,BI

145,000 (1000)

TH 1050

38 TO 44

B

170,000 (1178)

H 1075

31 TO 38

SSP

145,000 (1000)

TH 1075

37 TO 42

H 1100

30 TO 37

B,F,T,BI

140,000 (965)

TH 1100

34 TO 39

H 1100

30 TO 37

SSP

140,000 (965)

CH 900

46 MIN

SS

(2)

H 1100

30 TO 37

C

130,000 (895)

H 1150

28 TO 37

B,F,T,BI

135,000 (930)

H 1150

28 TO 37

SSP

135,000 (930)

NOTE (1)

B - BAR

H 1150M

24 TO 30

ALL

F - FORGINGS

T - TUBING

PH 13-8 MO

H 950

45 TO 49

B,F,T,BI,P

220,000 (1520)

Bi - BILLET

H 1000

43 TO 47

B,F,T,BI,P

205,000 (1415)

SSP - SHEET, STRIP, PLATE

H 1025

41 TO 46

B,F,T,BI,P

185,000 (1275)

P - PLATE

H 1050

40 TO 46

B,F,T,BI,P

175,000 (1210)

WT - WELDED TUBING

H 1100

34 TO 42

B,F,T,BI,P

150,000 (1035)

H 1150

30 TO 38

B,F,T,BI,P

135,000 (930)

NOTE (2)

VARIES WITH THICKNESS

H 1150M

28 TO 36

AMS 2759/3 TABLE III

PAGE 2 OF 2

ALLOY

CONDITION

HARDNESS

FORM (1)

TENSILE PSI

ALLOY

CONDITION

HARDNESS

FORM (1)

TENSILE PSI

HRC

(MPa)

HRC

(MPa)

PH 14-8 MO

SRH 950

45 TO 51

SSP

220,000 (1520)

AM-355

SCT 850

41 TO 47

SSP

190,000 (1310)

SRH 1050

38 TO 45

SSP

200,000 (1380)

SCT 1000

37 TO 43

B,F,T

170,000 (1175)

SCT 1000

38 TO 44

SSP

165,000 (1140)

PH 15-7 MO

RH 950

46 TO 50

SSP

225,000 (1555)

RH 950

46 TO 50

B

200,000 (1300)

CUSTOM 450

H 900

39 MIN

WROUGHT

180,000 (1240)

RH 1000

42 TO 46

H 950

37 MIN

RH 1100

34 TO 42

H 1000

36 MIN

TH 1000

SSP

205,000 (1415)

H 1050

34 MIN

WROUGHT

145,000 (1000)

TH 1050

40 TO 46

SSP

190,000 (1310)

H 1100

30 MIN

TH 1050

40 TO 46

B

170,000 (1175)

H 1150

26 MIN

TH 1075

39 TO 44

TH 1100

36 TO 41

CUSTOM 455

H 900

47 MIN

CH 900

46 MIN

SS

240,000 (1655)

H 950

45 MIN

WROUGHT

225,000 (1555)

H 1000

44 MIN

WROUGHT

200,000 (1380)

A-286

24 TO 35

SHEET, P

125,000 (860 MPA)

24 TO 36

ALL

130,000 (895 MPA)

MARAGING 250

AGED

49 TO 52

24 TO 37

SHEET, P

135,000 (930 MPA)

24 TO 38

SHEET, P

140,000 (965 MPA)

MARAGING 300

AGED

52 TO 56

29 TO 38

B,F

140,000 (965 MPA)

40 MIN

B, WIRE

200,000 (1380 MPA)

NOTE (1)

B - BAR

F - FORGINGS

AM-350

SCT 850

41 TO 48

SSP,T

185,000 (1278)

T - TUBING

SCT 950

38 TO 45

SSP,T

170,000 (1175)

Bi - BILLET

SCT1000

36 TO 43

B,F,T

165,000 (1140)

SSP - SHEET, STRIP, PLATE

SCT 1100

35 TO 42

P - PLATE

WT - WELDED TUBING

NOTE (2)

VARIES WITH THICKNESS