ALLOY

CONDITION

HARDNESS

FORM (1)

TENSILE PSI

HRC

(MPa)

15-5 PH

H 900

40 TO 47

B,F,T,BI

190,000 (1310)

AND

H 900

40 TO 47

SSP

190,000 (1310)

17-4 PH

H 900

40 TO 47

C

180,000 (1240)

H 925

38 TO 45

B,F,T,BI

180,000 (1240)

H 925

38 TO 45

SSP

170,000 (1175)

H 925

38 TO 45

C

170,000 (1175)

H 950

37 TO 44

WROUGHT

165,000 (1140)

H 1000

36 TO 43

C

150,000 (1035)

H 1025

34 TO 42

B,F,T,BI

155,000 (1070)

H 1025

34 TO 42

SSP

155,000 (1070)

H 1050

32 TO 38

B,F,T,BI

150,000 (1035)

H 1075

31 TO 38

B,F,T,BI

145,000 (1000)

H 1075

31 TO 38

SSP

145,000 (1000)

H 1100

30 TO 37

B,F,T,BI

140,000 (965)

H 1100

30 TO 37

SSP

140,000 (965)

H 1100

30 TO 37

C

130,000 (895)

H 1150

28 TO 37

B,F,T,BI

135,000 (930)

H 1150

28 TO 37

SSP

135,000 (930)

H 1150M

24 TO 30

ALL

17-7 PH

RH 950

42 TO 49

SS

210,000 (1450)

RH 950

42 TO 49

P

200,000 (1380)

RH 950

42 TO 49

B

185,000 (1275)

RH 1000

41 TO 46

RH 1050

40 TO 45

SSP

180,000 (1240)

RH 1050

40 TO 45

B

170,000 (1175)

RH 1075

38 TO 43

RH 1100

34 TO 40

WROUGHT

150,000 (1035)

TH 950

42 TO 48

TH 1000

40 TO 46

TH 1050

38 TO 44

SSP,WT

180,000 (1240)

TH 1050

38 TO 44

B

170,000 (1178)

TH 1075

37 TO 42

TH 1100

34 TO 39

CH 900

46 MIN

SS

(2)

HRC

(MPa)

PH 14-8 MO

SRH 950

45 TO 51

SSP

220,000 (1520)

SRH 1050

38 TO 45

SSP

200,000 (1380)

PH 15-7 MO

RH 950

46 TO 50

SSP

225,000 (1555)

RH 950

46 TO 50

B

200,000 (1300)

RH 1000

42 TO 46

RH 1100

34 TO 42

TH 1000

SSP

205,000 (1415)

TH 1050

40 TO 46

SSP

190,000 (1310)

TH 1050

40 TO 46

B

170,000 (1175)

TH 1075

39 TO 44

TH 1100

36 TO 41

CH 900

46 MIN

SS

240,000 (1655)

A-286

24 TO 35

SHEET, P

125,000 (860 MPA)

24 TO 36

ALL

130,000 (895 MPA)

24 TO 37

SHEET, P

135,000 (930 MPA)

24 TO 38

SHEET, P

140,000 (965 MPA)

29 TO 38

B,F

140,000 (965 MPA)

40 MIN

B, WIRE

200,000 (1380 MPA)

AM-350

SCT 850

41 TO 48

SSP,T

185,000 (1278)

SCT 950

38 TO 45

SSP,T

170,000 (1175)

SCT1000

36 TO 43

B,F,T

165,000 (1140)

SCT 1100

35 TO 42

AM-355

SCT 850

41 TO 47

SSP

190,000 (1310)

SCT 1000

37 TO 43

B,F,T

170,000 (1175)

SCT 1000

38 TO 44

SSP

165,000 (1140)

CUSTOM 450

H 900

39 MIN

WROUGHT

180,000 (1240)

H 950

37 MIN

H 1000

36 MIN

H 1050

34 MIN

WROUGHT

145,000 (1000)

H 1100

30 MIN

H 1150

26 MIN

CUSTOM 455

H 900

47 MIN

H 950

45 MIN

WROUGHT

225,000 (1555)

H 1000

44 MIN

WROUGHT

200,000 (1380)

MARAGING 250

AGED

49 TO 52

MARAGING 300

AGED

52 TO 56

NOTE (1)

B - BAR

F - FORGINGS

T - TUBING

Bi - BILLET

SSP - SHEET, STRIP, PLATE

P - PLATE

WT - WELDED TUBING

NOTE (2)

VARIES WITH THICKNESS